   1 # Batch 2019.06.21 #
   2
   3 A total of 12 3" KNSB grains for 54mm cases.  These were cast in two batches
   4 that each consisted of a two 9" casting tubes, one each with 0.5 inch steel
   5 and 0.625 inch Delrin cores.  One batch was pure KNSB, the other was my usual
   6 mixture with RIO and Polystep-B1 surfactant.  Simple pour, insert coring rod,
   7 top off grain.  No vacuum processing or vibration.
   8
   9 The 54mm casting tube I'm using weighs 1.9g per inch.
  10
  11 The purpose of casting these grains is to do test stand burns of identical
  12 motors in each of the two propellant variants, so I can tell how much the
  13 RIO is affecting ignitability and burn rate.
  14
  15 These grains were cast on 2019-06-21.
  16
  17 ## Results ##
  18
  19 The batch size was pretty good, there was a bit of excess propellant in each
  20 batch so we can make density and burn rate measurements after cure.  The excess
  21 weighed in at g after cure.
  22
  23 Grains were cut, core drilled to 0.625", and sanded more or less ala Terry's
  24 process.  In the data below, lengths are a bit approximate due to imperfectly
  25 squared ends, gross masses are precise using my new 600g by 0.01g scale!
  26
  27 Batch with RIO:
  28
  29 * Grain 1, " long, g gross, g casting tube, g net
  30 * Grain 2, " long, g gross, g casting tube, g net
  31 * Grain 3, " long, g gross, g casting tube, g net
  32 * Grain 4, " long, g gross, g casting tube, g net
  33 * Grain 5, " long, g gross, g casting tube, g net
  34 * Grain 6, " long, g gross, g casting tube, g net
  35
  36 Batch without RIO:
  37
  38 * Grain 7, " long, g gross, g casting tube, g net
  39 * Grain 8, " long, g gross, g casting tube, g net
  40 * Grain 9, " long, g gross, g casting tube, g net
  41 * Grain 10, " long, g gross, g casting tube, g net
  42 * Grain 11, " long, g gross, g casting tube, g net
  43 * Grain 12, " long, g gross, g casting tube, g net
  44
  45 The mass per unit length was within ?g/inch.