   1 # Batch 2019.06.21 #
   2
   3 A total of 12 3" KNSB grains for 54mm cases.  These were cast in two batches
   4 that each consisted of a two 9" casting tubes, one each with 0.5 inch steel
   5 and 0.625 inch Delrin cores.  One batch was pure KNSB, the other was my usual
   6 mixture with RIO and Polystep-B1 surfactant.  Simple pour, insert coring rod,
   7 top off grain.  No vacuum processing or vibration.
   8
   9 The 54mm casting tube I'm using weighs 1.9g per inch.
  10
  11 The purpose of casting these grains is to do test stand burns of identical
  12 motors in each of the two propellant variants, so I can tell how much the
  13 RIO is affecting ignitability and burn rate.
  14
  15 These grains were cast on 2019-06-21.
  16
  17 ## Results ##
  18
  19 Batch with RIO:
  20
  21 * Grain 1, " long, 0.5" core, g gross, g casting tube, g net
  22 * Grain 2, " long, 0.5" core, g gross, g casting tube, g net
  23 * Grain 3, " long, 0.5" core, g gross, g casting tube, g net
  24
  25 * Grain 4, " long, 0.625" core, g gross, g casting tube, g net
  26 * Grain 5, " long, 0.625" core, g gross, g casting tube, g net
  27 * Grain 6, " long, 0.625" core, g gross, g casting tube, g net
  28
  29 Batch without RIO:
  30
  31 * Grain 7, " long, 0.5" core, g gross, g casting tube, g net
  32 * Grain 8, " long, 0.5" core, g gross, g casting tube, g net
  33 * Grain 9, " long, 0.5" core, g gross, g casting tube, g net
  34
  35 * Grain 10, " long, 0.625" core, g gross, g casting tube, g net
  36 * Grain 11, " long, 0.625" core, g gross, g casting tube, g net
  37 * Grain 12, " long, 0.625" core, g gross, g casting tube, g net
  38
  39 The mass per unit length was within ?g/inch.