git.gag.com Git - web/gag.com/blob - rockets/research/2018-batch-01.mdwn

   1 # Batch 2018-batch-01 #
   2
   3 A slightly improved "repeat performance" M reload for my CTI Pro75 6xl case
   4 with Loki nozzle and forward closure.
   5
   6 Using Terry's #50 "short" Loki nozzle, we need a 38" liner and have just
   7 under 37" available for fuel.  Using dash-143 buna-n o-rings as grain
   8 spacers, let's try 7 grains of 5.205" length, or 132mm, using Delrin coring
   9 rods of 0.75" diameter.  This will be slightly more progressive than the
  10 8-brain config last fall, but all parameters look good and it's a tad more
  11 propellant due to one less inter-grain gap.
  12
  13 The simulator says this could be a 34% M-2593.
  14
  15 Based on previous experience, there will be enough shrinkage to necessitate
  16 a "topping up" of each grain after the initial pour cools.
  17
  18 The simulator says we need 4919g of fuel for these grains, so let's melt a
  19 batch size of 5kg:
  20
  21 * 65% KNO3, 3250g
  22 * 35% Sorbitol, 1750g
  23 * 1% red iron oxide, 50g, added after melt
  24 * 75 drops Polystep-B1, added before pour using eye dropper
  25
  26 This formula is completely fluid with 225F indicated on the Presto Multicooker,
  27 but viscosity is noticeabley lower making for easier pouring at 250-275F.
  28
  29 These grains were cast on <date>.
  30
  31 ## Results ##
  32
  33 Average casting tube weight <mumble>g.
  34
  35 * Grain 1, g gross, g net
  36 * Grain 2, g gross, g net
  37 * Grain 3, g gross, g net
  38 * Grain 4, g gross, g net
  39 * Grain 5, g gross, g net
  40 * Grain 6, g gross, g net
  41 * Grain 7, g gross, g net
  42
  43 Total propellant load <mumble>g.
  44
  45 Revised simulation says this will be...