   1 # Test 4 #
   2
   3 More KNER grains.  Since we had 8 plausible grains from test 3 and
   4 want to burn 5 at a time, we decided to cast another 4 so we'd have
   5 enough for two motors plus a couple single-grain open air burn tests.
   6
   7 Formula is a simple mix of 65% KNO3 and 35% Erythritol.  Both used in
   8 granular form directly from stock.  A 275 gram batch for 4 2.25"
   9 38mm grains.
  10
  11 Used our new casting bases, now with the mandrel holes drilled all the
  12 way through.
  13
  14 ## Process ##
  15
  16 Same as Test 3B.
  17
  18 ## Results ##
  19
  20 * Test 4, Grain 1, 61.50g net
  21 * Test 4, Grain 2, 62.38g net
  22 * Test 4, Grain 3, 60.18g net
  23 * Test 4, Grain 4, excessive visible inclusions, set aside
  24
  25 ## Observations ##
  26
  27 Not surprisingly, results were essentially identical to test 3B.
  28
  29 Seems pretty clear that the post-casting process of having to cut off
  30 the "skin" at the top of the grain and impart a concave shape is
  31 losing .. means we'll never get uniform grain masses.  REally need
  32 to figure out how to do this better.
  33
  34 The last grain was "poured" by spooning in material that seemed