git.gag.com Git - web/gag.com/blob - rockets/research/test11.mdwn

   1 # Test 11 #
   2
   3 Our first attempt at making 54mm grains with sorbitol.  Grain length 3.25",
   4 core diameter 0.5" (only mandrels on hand).  Casting tubes from
   5 [ARR](http://www.alwaysreadyrocketry.com/), machined a new set of hardwood
   6 casting stands on our CNC router, drilled PVC pipe caps for upper mandrel
   7 centering.
   8
   9 The formula used is the same we've been using with sorbitol, but in an 875g
  10 batch this time:
  11
  12 * 65% KNO3, 568.75g, taken from the big bucket this time
  13 * 35% Sorbitol, 306.25g
  14 * 1% red iron oxide, 8.75g, added after melt
  15 * 10 drops Polystep-B1, added before pour using eye dropper
  16
  17 Robert noted that tamping down the material in the grains required a tweak
  18 to his process for 38mm, since the larger casting tubes and greater propellant
  19 mass meant having to hold everything together more solidly.  We also noted
  20 that there was some variation (a mm or so?) in my casting tube lengths, so
  21 getting them uniformly filled was a bit fiddly.  Our calculations led us to
  22 use a fill line 76.118mm from the bottom or 6.431mm from the top of the
  23 casting tubes.  On a couple of the shortest-cut casting tubes, this led to a
  24 small amount of propellant contacting the inside of the pipe cap.  Try harder
  25 to cut precisely next time!
  26
  27 These grains were cast on 1 September 2015.
  28
  29 ## Results ##
  30
  31 Dropped one grain at home, big chunk missing and maybe cracks.  Decided not
  32 to use it.  That left us with three "good" grains.
  33
  34 The case, nozzle, and closure combination used left me cutting the liner to
  35 10.250 inches, while Loki specifies 10.375 for their 3-grain case.  The total
  36 available propellant length was 9.459", so I had to trim the three grains
  37 slightly to fit.  The gross masses below were post-trim.  Calculating net
  38 masses will require approximation based on the overall casting tube length
  39 that remained.
  40
  41 * Grain 1, ?g net
  42 * Grain 2, 204.0g gross, ?g net
  43 * Grain 3, 199.3g gross, ?g net
  44 * Grain 4, 198.6g gross, ?g net
  45
  46 10.250" liner, 8.3mm nozzle throat, buna-n o-rings.
  47
  48 calculated as a 39% J-477, 843 Ns, ~1.5 sec burn
  49
  50 ## Observations ##
  51
  52 1250g pre-launch motor mass, 664g post-flight motor mass.
  53
  54 4830g pre-launch airframe mass.