git.gag.com Git - web/gag.com/blob - rockets/research/2017-batch-09.mdwn

   1 # Batch 2017-batch-09 #
   2
   3 8 grains of 75mm using sorbitol, intended to be a reload for my CTI Pro75 6xl
   4 case with Loki nozzle and forward closure.  Grain length 4.375" with 0.125"
   5 spacing per grain, so we'll make the casting tubes 4.5" long.  Delrin coring
   6 rods of 0.75" diameter.
   7
   8 To overcome shrinkage noticed in the last batch, fill lines set based on the
   9 total 4.5" casting tube length, on the assumption that any shrinkage will
  10 provide sufficient inter-grain spacing.
  11
  12 Formula for a batch size of 4800g:
  13
  14 * 65% KNO3, 3120g
  15 * 35% Sorbitol, 1680g
  16 * 1% red iron oxide, 48g, added after melt
  17 * 72 drops Polystep-B1, added before pour using eye dropper
  18
  19 This formula is completely fluid with 225F indicated on the Presto Multicooker,
  20 but viscosity is noticeabley lower making for easier pouring at 250-275F.
  21
  22 These grains were cast on 15 October 2017.
  23
  24 ## Results ##
  25
  26 This batch made for a pretty full Presto, and a fairly long time coming up
  27 to temperature.  It seems like 5kg might be the most propellant I should try
  28 to melt at one time.  As an aside, that means for my 6" O project, we'd be
  29 melting and casting one grain at a time...
  30
  31 Average casting tube weight 15.3g.
  32
  33 * Grain 1, 542g gross, 527g net
  34 * Grain 2, 548g gross, 533g net
  35 * Grain 3, 552g gross, 537g net
  36 * Grain 4, 546g gross, 531g net
  37 * Grain 5, 544g gross, 529g net
  38 * Grain 6, 540g gross, 525g net
  39 * Grain 7, 528g gross, 513g net
  40 * Grain 8, 538g gross, 523g net
  41
  42 Total propellant load 4218g.  That's enough lower than the anticipated mass
  43 that I decided to "top off" the grains with more melted propellant from the
  44 left-overs in this batch.  Will re-weigh after they cool/cure.
  45