   1 # Batch 2017-batch-05 #
   2
   3 Another try at making our own igniters, using the "epoxy fire" formula from
   4 [Scott Berfield](http://www.berfield.com/igniters.html).  Moving from the
   5 pre-made ematches that "pop" to home-made wire-wound bridge wires with 6
   6 turns of 30ga nichrome wire, and we'll try the "slow" West Systems
   7 hardener.  We'll also try using slightly larger magnesium particles, sifted
   8 from the "saw chips" bag, not the powder.
   9
  10 Made up a 15g batch with the following formula:
  11
  12 * 68% KNO3, 10.20g, hand ground with mortar and pestle to fine grain size
  13 * 7% magnesium powder, 1.05g
  14 * 1% air float charcoal, 0.15g
  15 * 24% West Systems 105+206 epoxy, 3.60g
  16
  17 ** 3.03g 105 resin
  18 ** 0.57g 206 hardener
  19
  20 Two folded papers were used to weigh out the KNO3 in one, and a mixture of
  21 the magnesium powder and charcoal in another.  The epoxy was mixed in a small
  22 disposable plastic cup with a popsicle stick, then the magnesium and charcoal
  23 were poured in and mixed until complete wetted.  Then the KNO3 was added and
  24 mixed until everything became a homogenous mix.  It was a dry-ish, crumbly
  25 consistency, but packed into lumps easily.
  26
  27 Two sizes of plastic drinking straws used.  One is about 3/16-7/32" diameter,
  28 the other about 1/4" in diameter.  Both were cut into 1" lengths.  The
  29 procedure was to slide the
  30 ematch through the straw, pack material into the straw from the "back" end
  31 until it was mostly full, then pull the ematch lead until the match head was
  32 just at the forward end of the straw, then pack more material in the front
  33 end of the straw until the match head was just covered.  Using nitrile-gloved
  34 fingers, it was then easy to mash on both ends simultaneously to make sure
  35 we had good packing with minimal voids, leaving both ends flush with the
  36 straw.
  37
  38 The matches were left to cure overnight, and then the straws were carefully
  39 sliced lengthwise with a razor blade and peeled off, revealing what looked
  40 like very solid cylindrical igniters.  They look a lot like the Quickburst
  41 ones.
  42
  43 These igniters were made on 2 June 2017.
  44
  45 ## Results ##
  46
  47 We got 6 of the larger and 3 of the smaller igniters out of this batch.  It
  48 was very difficult to pack the smaller straws, probably due to the larger
  49 Mg particle size.  It could be that we need to go back to using the finer Mg
  50 powder when making smaller igniters, and reserve the "chunky" stuff for large
  51 ones?
  52
  53 ## Observations ##
  54