   1 # Batch 2017-batch-02 #
   2
   3 We're nearly out of [Quickburst](quickburst.net) igniters, they haven't been
   4 great at lighting erythritol grains anyway, and they're kind of
   5 expensive...  So we decided to experiment with making igniters, and the
   6 first ones we decided to try are "epoxy fire" using a formula from
   7 [Scott Berfield](http://www.berfield.com/igniters.html).
   8
   9 For our first attempt, we made up a 10g batch with the following formula:
  10
  11 * 68% KNO3, 6.80g, hand ground with mortar and pestle to fine grain size
  12 * 7% magnesium powder, 0.70g
  13 * 1% air float charcoal, 0.10g
  14 * 24% West Systems 105+205 epoxy, 2.40g
  15     * 2.01g 105 resin
  16     * 0.39g 205 hardener
  17
  18 Two folded papers were used to weigh out the KNO3 in one, and a mixture of
  19 the magnesium powder and charcoal in another.  The epoxy was mixed in a small
  20 disposable plastic cup with a popsicle stick, then the magnesium and charcoal
  21 were poured in and mixed until complete wetted.  Then the KNO3 was added and
  22 mixed until everything became a homogenous mix.  It was a dry-ish, crumbly
  23 consistency, but packed into lumps easily.
  24
  25 We used Chinese made e-matches with 2m leads, and used plastic drinking straws
  26 about 1/4" in diameter cut into 1" lengths.  The procedure was to slide the
  27 ematch through the straw, pack material into the straw from the "back" end
  28 until it was mostly full, then pull the ematch lead until the match head was
  29 just at the forward end of the straw, then pack more material in the front
  30 end of the straw until the match head was just covered.  Using nitrile-gloved
  31 fingers, it was then easy to mash on both ends simultaneously to make sure
  32 we had good packing with minimal voids, leaving both ends flush with the
  33 straw.
  34
  35 The matches were left to cure overnight, and then the straws were carefully
  36 sliced lengthwise with a razor blade and peeled off, revealing what looked
  37 like very solid cylindrical igniters.  They look a lot like the Quickburst
  38 ones.
  39
  40 These igniters were made on 17 May 2017.
  41
  42 ## Results ##
  43
  44 They didn't work.  The basic problem is that the pyrogen on the Chinese
  45 e-matches is aggressive enough that they blow the end of the epoxy fire
  46 cylinder apart without igniting the rest of the igniter.  Next time we'll
  47 try with home-made bridge wires on shooter wire.
  48
  49 ## Observations ##
  50
  51 A 10g batch was just enough to make up 6 igniters, and the pot life seemed
  52 a little tight.  Next time, it seems like trying a 15g batch with the slower
  53 206 hardener might be a good plan?